Economical Pad Printing Silicone HY-901 for Flat Surface Daily Use Hongye Silicone

Features • 30 Shore A general hardness • 380 percent elongation, even imprint • Economical for small batch • 1 kg MOQ, ready stock • Room temp cure

Technical Parameters Model: HY-901 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.8 MPa | Tear Strength: 22±2 kN/m | Elongation: 380% | Mix Ratio: 100:2~100:3 | Density: 1.12±0.03 g/cm3 Model: HY-902 | Color: White | Hardness: 30±2 Shore A | Viscosity: 35000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 24±2 kN/m | Elongation: 430% | Mix Ratio: 100:2~100:3 | Density: 1.15±0.03 g/cm3 Model: HY-912 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 25±2 kN/m | Elongation: 340% | Mix Ratio: 100:2~100:3 | Density: 1.13±0.03 g/cm3 Model: HY-916 | Color: White | Hardness: 14±2 Shore A | Viscosity: 36000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.5 MPa | Tear Strength: 25±2 kN/m | Elongation: 570% | Mix Ratio: 100:2~100:3 | Density: 1.10±0.03 g/cm3

Applications Switch panels, battery covers, metal tags, PVC cards, packaging boxes.

Operation Weigh A, add catalyst 100:2 to 3, degas, pour, cure 3 to 4 h, demold.

Selection 901 economical flat, 902 arcs 430 percent, 912 high cycle high tear, 916 deep concave, 933 addition cure platinum.

Quality ISO 9001, COA per batch, RoHS REACH.

Packaging 1, 5, 20, 25 kg, 200 kg drums.

Ordering T/T PayPal, free samples, 1 to 2 days, sea air express from Shenzhen.

Support Custom formula, 10 years team.

Precautions Nitrile gloves, avoid sulfur amine tin phosphorus.

Storage Cool dry sealed, 12 months.

FAQ 901 for flat work, 902 for arcs, 912 for high cycle, 916 for deep recess.