High Tear Pad Printing Silicone 30 Shore A for High Volume Electronic and Plastic Transfer

HY-912 high tear Pad Printing Silicone is developed by Shenzhen Hongyejie Technology Co Ltd for high volume mass production scenarios. It enhances tear resistance in formula, achieving 25 plus or minus 2 kN per m tear strength. Uses condensation cure system with organotin catalyst, room temperature curing. 30 Shore A medium hardness provides even ink pickup and clear pattern transfer. Compared with economic grade, tear strength increases from 22kN per m to 25kN per m, extending pad head service life. ISO 9001 certified, exported to 138 countries.

Core Selling Points • High tear formula, 25 plus or minus 2 kN per m tear strength, resists tearing and cracking • 30 plus or minus 2 Shore A medium hardness for most scenarios • 4.0MPa tensile strength, good toughness • 340 percent elongation, good rebound, clear transfer • Even ink pickup, stable printing effect • Room temperature curing, easy operation • 100:2 to 100:3 mix ratio, flexible catalyst dosage • Low shrinkage, stable dimensions, high pattern fidelity • Long service life, thousands to tens of thousands of prints • Ideal for high volume mass production • COA report each batch • Multiple packaging options

Technical Parameters Model: HY-912 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 25±2 kN/m | Elongation: 340% | Mix Ratio: 100:2~100:3 | Density: 1.13±0.03 g/cm3 Model: HY-901 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.8 MPa | Tear Strength: 22±2 kN/m | Elongation: 380% | Mix Ratio: 100:2~100:3 | Density: 1.12±0.03 g/cm3 Model: HY-902 | Color: White | Hardness: 30±2 Shore A | Viscosity: 35000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 24±2 kN/m | Elongation: 430% | Mix Ratio: 100:2~100:3 | Density: 1.15±0.03 g/cm3 Model: HY-916 | Color: White | Hardness: 14±2 Shore A | Viscosity: 36000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.5 MPa | Tear Strength: 25±2 kN/m | Elongation: 570% | Mix Ratio: 100:2~100:3 | Density: 1.10±0.03 g/cm3

Application Scenarios

Electronic Appliance: Remote controls, chargers, small appliance panels, power adapters require printing logos, button markings, labels. High daily output and long machine running time demand durable pad heads. HY-912 at 25kN per m tear strength resists wear and cracking, extending pad head life by about 30 percent.

Plastic Gift: Keychains, badges, medallions, cosmetic cases, stationery require printing decorative patterns and text. Large orders with tight schedules need continuous production. HY-912 high tear resistance maintains stable quality during long hours of high frequency use.

Application and Operation Instructions

1. Prepare mold, clean surface, prepare materials and tools.
2. Weigh at 100:2 to 100:3 ratio.
3. Stir slowly 2 to 3 minutes.
4. Vacuum degas 3 to 5 minutes.
5. Pour slowly into mold from one side.
6. Cure 3 to 4 hours, demold, rest 24 hours.

Selection Guide HY-901 Economic: best cost performance for medium requirements. HY-902 Medium: better rebound for higher quality. HY-912 High Tear: longest life for high volume production. HY-916 Ultra Soft: for deep concave irregular surfaces.

Recommended Application High volume mass production in electronic appliance and plastic gift industries.

Quality and Compliance ISO 9001 certified, COA report each batch, RoHS and REACH compliant.

Packaging 1kg trial, 5kg, 20kg, 25kg, 200kg iron drum.

Competitive Advantages Own production lines, 100 tons monthly output, factory direct sales, stock available.

Ordering and Logistics T/T and Paypal, sample available, 1 to 3 days delivery, shipping from Shenzhen.

Technical Support Experienced team for consultation and custom formula service.

Precautions Nitrile gloves, avoid contact with tin sulfur amine, accurate weighing.

Storage Cool dry 5 to 30 degrees, 12 months shelf life, keep catalyst sealed.

FAQ Q: HY-912 vs HY-902? A: Both 30A and 4.0MPa. HY-912 has 25kN/m tear vs 24kN/m, longer life. HY-902 has 430 percent elongation vs 340 percent, better rebound. Q: Pad head lifespan? A: Thousands to tens of thousands of prints, about 30 percent longer than economic grade. Q: Catalyst amount? A: 100:2 to 100:3, do not exceed 100:4.